TECHNICAL SPECIFICATIONS
Diameter | 2.85 mm ± 0.10 mm |
Roundness | >95% |
RAL | 9003 |
Weight | 500 g |
Color | white |
MATERIAL PROPERTIES | |
Density | 1.31 g/cm3 (Test method: ISO 1183) |
MVR 230°C/2.16 kg | 10 cm3/10min (ISO 1133) |
MFR 230°C/2.16 kg | 13 gr/10 min (Test method: ISO 1133) |
Elongation at break | 130% (Test method: ISO 527) |
Tensile strength | 64 MPa (Test method: ISO 527) |
Tensile modulus | 2300MPa (Test method: ISO 527) |
Flexural modulus | 2100MPa (Test method: ISO 178) |
Flexural strength | 94 MPa (Test method: ISO 178) |
Impact strength – Charpy method 23°C | 9 kJ/m2 (Test method: ISO 179) |
Moisture absaorption | 0.2% (Test method: MCC Method) |
Coefficient of linear thermal expansion (-20~80°C) | 7.3E-05 (Test method: ISO 11359-2) |
Heat deflection temperature 1.80 MPa | 82°C (Test metod: ISO 75-1) |
Transparency | 2% (Test method: ISO 13468) |
RECOMMENDED PRINTER SET UP | |
Extrusion temperature | 225 – 245°C |
Melting temperature | 235°C |
Bed temperature | 85°C |
Printing speed | 50 mm/s |
Fan speed (can be changed to 0% is the model is warping) | 10% |